Specifications
| Specifications | |
|---|---|
| Classifications | EN ISO 14343-A : G 13 4 |
| Alloy Type | Martensitic-ferritic (12 % Cr – 4.5 % Ni – 0.5 % Mo) |
| Shielding Gas | M12, M13 (EN ISO 14175) |
| Typical Tensile Properties | |||
|---|---|---|---|
| Condition | Yield Strength | Tensile Strength | Elongation |
| As Welded | 860 MPa ( 125 ksi ) | 1050 MPa ( 152 ksi ) | 13 % |
| Stress Relieved 2 hour(s) 600 °C ( 1112 °F ) |
850 MPa ( 123 ksi ) | 900 MPa ( 131 ksi ) | 17 % |
| Stress Relieved 8 hour(s) 600 °C ( 1112 °F ) |
750 MPa ( 109 ksi ) | 850 MPa ( 123 ksi ) | 20 % |
| Typical Charpy V-Notch Properties | |
|---|---|
| Testing Temperature | Impact Value |
| 0 °C ( 32 °F ) | 35 J ( 26 ft-lb ) |
| 0 °C ( 32 °F ) | 70 J ( 52 ft-lb ) |
| 0 °C ( 32 °F ) | 75 J ( 55 ft-lb ) |
| -20 °C ( -4 °F ) | 30 J ( 22 ft-lb ) |
| -20 °C ( -4 °F ) | 55 J ( 40.5 ft-lb ) |
| -20 °C ( -4 °F ) | 75 J ( 55 ft-lb ) |
| Typical Weld Metal Analysis % | ||||||||
|---|---|---|---|---|---|---|---|---|
| C | Mn | Si | S | P | Ni | Cr | Mo | Cu |
| 0.02 | 0.38 | 0.37 | 0.003 | 0.019 | 4.5 | 12 | 0.4 | 0.1 |
| Typical Wire Composition % | ||||||||
|---|---|---|---|---|---|---|---|---|
| C | Mn | Si | S | P | Ni | Cr | Mo | Cu |
| 0.02 | 0.43 | 0.37 | 0.004 | 0.017 | 4.5 | 12.2 | 0.4 | 0.07 |
| Deposition Data | ||||
|---|---|---|---|---|
| Diameter | Current | Voltage | Wire Feed Speed | Deposition Rate |
| 0.8 mm ( .030 in. ) |
50-140 A | 16-22 V | 3.4-11 m/min ( 134-433 in./min ) |
0.8-2.7 kg/h ( 1.8-6.0 lbs/h ) |
| 0.9 mm ( .035 in. ) |
– | – | – | – |
| 1.0 mm ( .040 in. ) |
80-190 A | 16-24 V | 2.9-8.4 m/min ( 114-331 in./min ) |
1.1-3.1 kg/h ( 2.4-6.8 lbs/h ) |
| 1.2 mm ( .045 in. ) |
180-280 A | 20-28 V | 4.9-8.5 m/min ( 193-335 in./min ) |
2.6-4.5 kg/h ( 5.7-9.9 lbs/h ) |